Influencia del porcentaje de reemplazo de ceniza volante por cemento, sobre la resistencia a la compresión y absorción en la fabricación de adoquines de transito liviano

Simple item page
dc.contributor.advisorAlvarado Quintana, Hernán Martin
dc.contributor.authorBarrantes Villanueva, Jorge Alejandro
dc.contributor.authorHolguin Romero, Rita Cristina
dc.date.accessioned9/29/2016 11:01
dc.date.available9/29/2016 11:01
dc.date.issued2016
dc.descriptionEn la presente investigación se evaluó la influencia que tiene el porcentaje de ceniza volante por el reemplazo al cemento en adoquines modificados para transito liviano evaluando dicha influencia sobre la resistencia a la compresión y absorción. Las probetas se elaboraron según la norma NTP 399.611, en total se realizaron 30 probetas de 20 cm x 10 cm x 4 cm a base de arena, cemento, agua y ceniza volante. Los porcentajes de reemplazo que se utilizó en esta investigación fueron de 10, 20, 30, 40 y 50 % en peso. Las probetas se dejaron curar durante 28 días, para después realizar los ensayos de compresión y de absorción según las norma ASTM C109 y ASTM C20 respectivamente. De los resultados obtenidos se determina que cuando aumenta el porcentaje de reemplazo de ceniza volante por cemento, la resistencia a la compresión se incrementa moderadamente hasta un 20 % de reemplazo, a partir de allí la resistencia decae en un 9% al llegar al 30% de reemplazo de ceniza volante, en lo que respecta a la absorción esta propiedad tiene una relación lineal directa con el incremento en el porcentaje de reemplazo. Finalmente se determinó que un adoquín con 20% de ceniza volante de reemplazo origina mayor resistencia a la compresión que es 361.33 Kg/cm2 y un porcentaje de absorción de 5.32 % que están dentro de lo que especifica la Norma NTP 399.611. Concluyéndose que la ceniza volante tiene influencia en la resistencia a la compresión de un concreto modificado para adoquines afectando significativamente y en forma favorable.es_ES
dc.description.abstractIn this research the influence of the percentage of fly ash for cement replacement on modified light traffic paving stones for evaluating such influence on the compressive strength and absorption was assessed. The specimens were prepared according to standard NTP 399 611, in total 30 specimens of 20 cm x 10 cm x 4 cm made from sand, cement, water and fly ash is performed. Replacement percentages as used in this investigation were 10, 20, 30, 40 and 50% by weight. The specimens were allowed to cure for 28 days, and then performing compression tests and absorption according to ASTM C109 and ASTM C20 respectively From the results obtained it is determined that with increasing percentage replacement of fly ash cement, the compressive strength is moderately increased to 20% replacement, from there the resistance decays 9% reach 30% fly ash, in terms absorption this property has a direct linear relationship with the increase in the percentage of replacement. Finally it is determined that a paving stone with 20% fly ash replacement creates greater compressive strength is 361.33 kg / cm2 and its absorption percentage 5.32% are inside than specified by the standard NTP 399,611. Concluding that the fly ash has influence on the compressive strength of a concrete paver affecting significantly modified and favorably.es_ES
dc.identifier.urihttps://hdl.handle.net/20.500.14414/2550
dc.language.isospaes_ES
dc.publisherUniversidad Nacional de Trujillo
dc.relation.ispartofseriesTMAT 9034;9034
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/2.5/pe/
dc.sourceUniversidad Nacional de Trujilloes_ES
dc.sourceRepositorio institucional - UNITRUes_ES
dc.subjectFabricación de adoquines de transito livianoes_ES
dc.titleInfluencia del porcentaje de reemplazo de ceniza volante por cemento, sobre la resistencia a la compresión y absorción en la fabricación de adoquines de transito livianoes_ES
dc.typeinfo:eu-repo/semantics/bachelorThesises_ES
thesis.degree.disciplineMateriales
thesis.degree.grantorUniversidad Nacional de Trujillo.Facultad de Ingeniería
thesis.degree.levelTítulo Profesional
thesis.degree.nameIngeniero de Materiales
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
BARRANTES VILLANUEVA, Jorge Alejandro, HOLGUIN ROMERO, Rita.pdf
Size:
3.29 MB
Format:
Adobe Portable Document Format
Description:
FABRICACIÓN DE ADOQUINES DE TRANSITO LIVIANO
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
Tesis de Materiales