Vera Alvarado, Jorge WilfredoHidalgo Ruiz, Junior DanielSanchez Sanchez, Junnior Joel2024-01-262024-01-262023https://hdl.handle.net/20.500.14414/20515Medidas de dureza en componentes de construcción mecánica producen deformación plástica superficial en el material que ponen en riesgo su ciclo de servicio, dicha propiedad está íntimamente ligada a las características microestructurales del material, con lo cual se requiere métodos alternativos de carácter no destructivo que permitan predecir las propiedades mecánicas de un material. El objetivo del trabajo experimental fue determinar el efecto de estructuras modificadas micro estructuralmente por tratamientos térmicos de temple y revenido para acero de construcción mecánica en sus parámetros ultrasónicos. Fueron realizadas seis corridas experimentales en un horno eléctrico al variar la temperatura de temple con tres factores y revenido dos factores, las muestras de temple fueron enfriadas en agua para posterior revenido. Las muestras fueron caracterizadas por ensayos metalográficos, ultrasónicos y dureza. Las medidas de dureza incrementaron conforme incrementó la presencia de estructuras martensíticas en las muestras, produciendo un decremento en la velocidad y atenuación del haz. Las estructuras revenidas a 650 0C presentan mayor grado de transformación, respecto a las revenidas a 550 0C, es notorio el cambio morfológico que contrasta bien al disminuir la resistencia a la indentación y a la propagación del ultrasonido respecto a su condición inicial de temple.Hardness measurements in mechanical construction components produce superficial plastic deformation in the material that puts its service cycle at risk, this property is closely linked to the microstructural characteristics of the material, which requires alternative methods of a non- destructive nature that allow predicting the mechanical properties of a material. The objective of the experimental work was to determine the effect of structures modified microstructurally by heat treatments of quenching and tempering in a mechanical construction steel on its ultrasonic parameters. Six experimental runs were carried out in an electric furnace by varying the quenching temperature with three factors and tempering with two factors. The quenching samples were cooled in water for subsequent tempering. The samples were characterized by metallographic, ultrasonic and hardness tests. The hardness measurements increased as the presence of martensitic structures in the samples increased, producing a decrease in the speed and attenuation of the beam. The structures tempered at 650 0C present a higher degree of transformation, compared to those tempered at 550 0C, the morphological change is notorious, which contrasts well by decreasing the resistance to indentation and the propagation of ultrasound with respect to its initial tempering condition.application/pdfspainfo:eu-repo/semantics/openAccessAceroConstrucciones mecánicasinfo:eu-repo/semantics/bachelorThesishttps://purl.org/pe-repo/ocde/ford#2.00.00