Jáuregui Rosas, Segundo R.Castillo Jauregui, Luis Angel7/11/20177/11/20172011https://hdl.handle.net/20.500.14414/8151In this work a systematic investigation on the effect synthesis of temperature_x000D_ (from 0 to 40°C) and ageing time on the size and width of the energy band gap of_x000D_ ZnO nanoparticles, which have been synthesized by a modified Sol-Gel method, is_x000D_ reported. The optical properties of ZnO nanoparticles have been evaluated by_x000D_ their UV-vis absorption spectra, from which the size and energy band gap were_x000D_ obtained. The average of nanoparticle size ranged from 2.06nm to 6.78nm as the_x000D_ temperature was increased from 0ºC to 40°C, while the band gap decreases from_x000D_ 3.99eV to 3.46eV, respectively. A distribution of nanoparticle particle size also was_x000D_ observed for all temperatures and ageing timesEn este trabajo se reporta la investigación sistemática sobre el efecto de la_x000D_ temperatura de síntesis (entre 0 y 40°C) y el tiempo de envejecimiento en el_x000D_ tamaño y ancho de banda prohibida de nanopartículas de ZnO obtenidas por el_x000D_ método Sol-Gel modificado. Las propiedades ópticas de las nanopartículas de_x000D_ ZnO fueron evaluadas mediante espectroscopía UV-vis y su tamaño y ancho de_x000D_ banda prohibida fueron obtenidos a partir de sus espectros de absorción. El_x000D_ tamaño promedio de las nanopartículas abarcó desde 2.06nm a 6.78nm cuando la_x000D_ temperatura se incrementó de 0ºC a 40°C, mientras que el ancho de banda disminuyó_x000D_ de 3.99eV a 3.46eV, respectivamente. También se observó una distribución de_x000D_ tamaños de las nanopartículas para todas las temperaturas de síntesis y tiempos de_x000D_ envejecimientospainfo:eu-repo/semantics/openAccessNanopartículas, Oxido de Zinc, Banda prohibida, Sol-Gelinfo:eu-repo/semantics/bachelorThesis