Huamaní Muñoz, Balbín WilderVásquez Ibáñez, Marie France2018-12-272018-12-272018https://hdl.handle.net/20.500.14414/11083Objetivo: Comparar el Efecto Antibacteriano in vitro de los Cementos Selladores Endodónticos: Endofill, Sealapex, y AH Plus, frente a la Porphyromonas Endodontalis. Material y método: Se comparó el Efecto Antibacteriano in vitro de los Cementos Selladores Endodónticos: Endofill, Sealapex, y AH Plus, frente a la Porphyromonas Endodontalis. Para ello se realizó el cultivo de la bacteria y colocación de los diferentes cementos selladores endodónticos, por 24 horas; para luego medir en mm. los halos de inhibición según la escala de Duraffourd. Resultados: El Efecto antibacteriano in vitro de los Cementos Selladores Endodónticos: se observó que el sellador a base de óxido de zinc y eugenol (Endofil) y el sellador a base de resina epóxica (AH Plus) fueron efectivos; mientras que el sellador a base de hidróxido de calcio Sealapex no fue efectivo frente a la Porphyromonas Endodontalis. Conclusión: La bacteria de la Porphyromonas Endodontalis es más susceptible al cemento sellador Endofill, observándose halos menores; mientras que con el cemento sellador a base de hidróxido de calcio (Sealapex) no fue efectiva; presentando una desviación estándar de 11.1Objective: To compare the in vitro antibacterial effect of Endodontic Sealant Cements, Endofill, Sealapex, and AH Plus, against Porphyromonas Endodontalis. Material and method: The in vitro antibacterial effect of Endodontic Sealant Cements was compared: Endofill, Sealapex, and AH Plus, against Porphyromonas Endodontalis. To do this, the bacteria were cultivated and the different endodontic sealant cements were placed for 24 hours; to then measure in mm. inhibition halos according to the Duraffourd scale. Results: The in vitro antibacterial effect of endodontic sealant cements: it was observed that the sealant based on zinc oxide and eugenol (Endophil) and the epoxy resin based sealer (AH Plus) were effective; while Sealapex calcium hydroxide based sealant was not effective against Porphyromonas Endodontalis. Conclusion: Porphyromonas Endodontalis bacteria are more susceptible to Endofill sealer cement, with minor haloes being observed; whereas with the cement sealer based on calcium hydroxide (Sealapex) it was not effective; presenting a standard deviation of 11.1.info:eu-repo/semantics/openAccessBacilos anaerobios gramnegativoEfecto de la Sustancia QuìmicaActividad Bacterianainfo:eu-repo/semantics/bachelorThesis