Vega Anticona, AlexanderAredo Sanchez, Meisy LisethSalirrosas Sanchez, Elfer Ismael2024-11-062024-11-062024-11https://hdl.handle.net/20.500.14414/22808En la presente investigación se extrajeron fibras de las hojas de piña Golden, se le realizo un tratamiento alcalino durante (1 hora- 25°C, con agua destilada), a diferentes concentraciones (0, 4, 8 y 12) g/L de KOH; se caracterizó mediante análisis de composición química, Espectroscopia Infrarroja por Transformada de Fourier (FTIR), Microscopia Electrónica de Barrido (SEM) y % de absorción de agua de las fibras ; se elaboraron placas de resina poliéster, compuesto (poliéster + 3 capas de fibra de vidrio), compuesto (poliéster + fibras de hojas de piña) y compuesto hibrido (poliéster + 2 capas de fibra de vidrio + fibras de hojas de piña), variando el % en peso de (15, 25 y 35)% de fibra en forma unidireccional continua para cada nivel de tratamiento; con dimensiones de (100 x 85 x 4) mm por el método de conformado a compresión en molde metálico a temperatura ambiente, se realizó el corte de estas placas (norma UNE EN ISO 179-1) con medida de (80 x 10 x 4) mm de largo, ancho y espesor; posteriormente se hizo el ensayo al impacto (ASTM D 6110); como resultados para la caracterización de la fibra se concluye que: conforme aumenta la concentración de KOH las fibras tienen mayor porcentaje de (celulosa y lignina), contenido variable de hemicelulosa, y menores impurezas (grasas y cenizas); menor absorción de agua, debido a que este elimina impurezas y componentes hidrofílicos de la fibra, en las imágenes SEM se observó cambio en la rugosidad superficial con una fibra más limpia. Los resultados de resistencia al impacto de las probetas fueron: 6.67 KJ/𝑚2 para la resina poliéster, 38.35 KJ/𝑚2 para el (C-FV), 6.89 KJ/𝑚2 para el (C-FP/SMQ-15%) y 26.51 KJ/𝑚2 para el (C-FP12g/L-35%), 33.57 KJ/𝑚2 para el (CH/SMQ-15%) y 52.78 KJ/𝑚2 para el (CH/12g/L-35%). Con lo que se pudo concluir que conforme se incrementa las concentraciones del KOH y los % en peso de fibra de piña mejora la resistencia al impacto del compuesto hibrido, debido a que se modifica la rugosidad superficial de la fibra y se aumenta el área de contacto fibra-matriz lo cual permitirá una mayor transferencia de cargas. Palabras claves: tratamiento alcalino, matriz, hibrido ABSTRACT In this research, some fibers were extracted from Golden pineapple leaves, an alkaline treatment was carried out for (1 hour- 25 ° C, with distilled water), at different concentrations (0, 4, 8 and 12) g / L of KOH; it was characterized by chemical composition analysis, Fourier Transform Infrared Spectroscopy (FTIR), Scanning Electron Microscopy (SEM) and % of water absorption of the fibers; plates of polyester resin, composite (polyester + 3 layers of fiberglass), composite (polyester + pineapple leaf fibers) and hybrid composite (polyester + 2 layers of fiberglass + pineapple leaf fibers) were made, varying the weight % of (15, 25 and 35)% of fiber in a continuous unidirectional form for each treatment level; with dimensions of (100 x 85 x 4) mm by the compression forming method in a metal mold at room temperature, these plates were cut (UNE EN ISO 179-1 standard) with measurements of (80 x 10 x 4) mm in length, width and thickness; subsequently the impact test was performed (ASTM D 6110); as results for the characterization of the fiber it is concluded that: as the KOH concentration increases the fibers have a higher percentage of (cellulose and lignin), variable hemicellulose content, and lower impurities (fats and ashes); lower water absorption, because this eliminates impurities and hydrophilic components of the fiber, in the SEM images a change in surface roughness was observed with a cleaner fiber. The impact resistance results of the test pieces were: 6.67 KJ/m2 for the polyester resin, 38.35 KJ/m2 for the (C-FV), 6.89 KJ/m2 for the (C-FP/SMQ-15%) and 26.51 KJ/m2 for the (C-FP12g/L-35%), 33.57 KJ/m2 for the (CH/SMQ-15%) and 52.78 KJ/m2 for the (CH/12g/L-35%). From which it was concluded that as the concentrations of KOH and the % by weight of pineapple fiber increase, the impact resistance of the hybrid composite improves, because the surface roughness of the fiber is modified and the fiber-matrix contact area is increased, which will allow a greater transfer of loads. Keywords: alkaline treatment, matrix, hybridapplication/pdfspainfo:eu-repo/semantics/openAccessTECHNOLOGY::Engineering physics::Other engineering physicsinfo:eu-repo/semantics/bachelorThesishttps://purl.org/pe-repo/ocde/ford#2.05.00