Efecto de la temperatura de envejecimiento del tratamiento térmico T6 sobre la resistencia de tracción, ductilidad, impacto, desgaste y dureza en la aleación Zn-22Al

Simple item page
dc.contributor.advisorPurizaga Fernández, Ismael Ignacio
dc.contributor.authorCipriano Burgos, César Eduardo
dc.contributor.authorRodríguez Mauricio, Pedro Raúl
dc.date.accessioned2025-04-29T19:14:50Z
dc.date.available2025-04-29T19:14:50Z
dc.date.issued2025-04
dc.description.abstractLa investigación estudió el efecto de la temperatura de envejecimiento dentro del tratamiento térmico T6 (disolución + envejecimiento) en la aleación aluminio zinc – 22% aluminio (ZA-22) colada en molde de arena sobre resistencia a la tracción (MPa), ductilidad (% elongación), resistencia al impacto (J), resistencia al desgaste (mg) y dureza (HB). Las propiedades mecánicas mencionadas se evaluaron con técnicas y métodos normalizado, y utilizando probetas estandarizadas; para el ensayo de tracción se utilizó la norma ASTM E-8, para el ensayo de resistencia al impacto tipo Charpy se utilizó la norma ASTM E23-98, para el ensayo de resistencia al desgaste se utilizó la norma ASTM G-77 y para el ensayo de dureza se utilizó la norma ASTM E-10. El rango de temperaturas de envejecimiento seleccionado para la investigación fue de 100, 140, 180, 220 y 260ºC. Los resultados obtenidos mostraron que a una temperatura de envejecimiento de 180ºC por 3 horas, se observan los mejores valores de las propiedades mecánicas estudiadas; a esta temperatura de envejecimiento; las probetas previamente con tratamiento de disolución a 360ºC por 1 hora con temple en agua; microestructuralmente ocurre la mayor redistribución de los componentes aleantes y se produce la precipitación de partículas de fase gamma de partículas de manera uniforme que actúan como obstáculos para el movimiento de las dislocaciones haciendo a la aleación más resistente. Con una temperatura de envejecimiento mayor hasta 260ºC se produce una disminución de los valores de las propiedades mecánicas estudiadas que se debe al “sobreenvejecimiento”, lo que produce un aumento de tamaño grano de las partículas precipitadas distorsionando la matriz de manera no homogénea.
dc.description.tableofcontentsThe research studied the effect of aging temperature within the T6 heat treatment (solution + aging) on the tensile strength (MPa), ductility (% elongation), impact resistance (J), wear resistance (mg), and hardness of the aluminum-zinc alloy – 22% aluminum (ZA-22) cast in sand mold. (HB). The aforementioned mechanical properties were evaluated using standardized techniques and methods, and standardized specimens; for the tensile test, the ASTM E-8 standard was used, for the Charpy impact test, the ASTM E23-98 standard was used, for the wear resistance test, the ASTM G-77 standard was used, and for the hardness test, the ASTM E-10 standard was used. The range of aging temperatures selected for the research was 100, 140, 180, 220, and 260ºC. The results obtained showed that at an aging temperature of 180ºC for 3 hours, the best values of the studied mechanical properties were observed; at this aging temperature, the samples previously subjected to a solution treatment at 360ºC for 1 hour with water quenching; microstructurally, the greatest redistribution of alloying components occurs and the precipitation of gamma phase particles occurs uniformly, acting as obstacles to dislocation movement, making the alloy more resistant. With an aging temperature of up to 260ºC, a decrease in the values of the studied mechanical properties occurs due to "over-aging," which results in an increase in the grain size of the precipitated particles, distorting the matrix in a non-homogeneous manner.
dc.formatapplication/pdf
dc.identifier.urihttps://hdl.handle.net/20.500.14414/23929
dc.language.isospa
dc.publisherUniversidad Nacional de Trujillo
dc.publisher.countryPE
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rights.urihttps://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subjectTECHNOLOGY::Chemical engineering::Metallurgical process and manufacturing engineering::Metallurgical process engineering
dc.subject.ocdehttps://purl.org/pe-repo/ocde/ford#2.00.00
dc.titleEfecto de la temperatura de envejecimiento del tratamiento térmico T6 sobre la resistencia de tracción, ductilidad, impacto, desgaste y dureza en la aleación Zn-22Al
dc.typeinfo:eu-repo/semantics/bachelorThesis
dc.type.versioninfo:eu-repo/semantics/publishedVersion
renati.advisor.dni17806774
renati.advisor.orcid0000-0001-7434-7336
renati.author.dni7097009
renati.author.dni70227090
renati.discipline713026
renati.jurorAguilar Rodriguez, Luis Wilfredo
renati.jurorCastillo Chung, Aldo Roger
renati.jurorPurizaga Fernandez, Ismael Ignacio
renati.levelhttps://purl.org/pe-repo/renati/level#tituloProfesional
renati.typehttps://purl.org/pe-repo/renati/type#tesis
thesis.degree.disciplineIngenieria Metalurgica
thesis.degree.grantorUniversidad Nacional de Trujillo. Facultad de Ingenieria
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
Cipriano Burgos y Rodriguez Mauricio.pdf
Size:
2.52 MB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
Tesis de Metalúrgica