Influencia de la presión de infiltración del proceso de moldeo por trasferencia de resina, sobre la resistencia a la tracción, de un compuesto de matriz poliéster reforzada con fibra de vidrio

Simple item page
dc.contributor.advisorVega Anticona, Alexander Yushepy
dc.contributor.authorRodriguez D’Angelo, David Alessandro
dc.contributor.authorSaucedo Fernández, Homero
dc.date.accessioned9/29/2016 9:18
dc.date.available9/29/2016 9:18
dc.date.issued2016
dc.descriptionEn el presente trabajo, se investigó el efecto de la presión de infiltración del proceso de moldeo por transferencia de resina (RTM), sobre la resistencia máxima a la tracción en laminados de matriz poliéster reforzada con fibra de vidrio E corta y al azar, los valores de presión de infiltración evaluados fueron de 30,45,60,75 y 90 psi, para el proceso de RTM se adaptó una compresora de aire de 2 HP de potencia, los laminados obtenidos mediante los procesos mencionados fueron de 30 * 15 cm de largo y ancho; el espesor estuvo determinado por el espesor del molde en el caso de RTM fue de 3 mm aproximadamente. De los laminados obtenidos se extrajeron probetas para el ensayo de tracción según la norma ASTM D638–01. De los resultados obtenidos se determinó que el incremento de la presión de infiltración en el rango de estudio, incrementa la resistencia máxima a la tracción de los laminados obtenidos mediante el proceso de RTM, en el rango de 30 a 75 psi (90.21 y 128.96 MPa respectivamente), para luego presentar una ligera disminución de dicha propiedad a los 90psi (123.58 MPa), ello dependería de las características de permeabilidad de las capas de refuerzo y del fenómeno que denominamos desplazamiento, además de la falta de humectación de la fibras utilizadas por parte de la resina. Los valores más altos de resistencia a la tracción se alcanzaron a los 75 psi (128.96 MPa), mientras que los más bajos, se obtuvieron a los 30 psi (90.21MPa). En algunos casos se evidencia desprendimiento entre fibra y matriz indicando o mostrando la falta de humectación entre los componentes del compuesto obtenido, ello se evidencio a través de evaluación micrográfica. Los resultados son confirmados mediante análisis de varianza para un nivel de confianza de 95%, concluyéndose que la presión de infiltración de resina influyen significativamente en la resistencia máxima a la tracción de los laminados de resina poliéster y fibra de vidrio obtenidos mediante el proceso de RTM.es_ES
dc.description.abstractIn this work, the effect of the pressure infiltration process of resin transfer molding (RTM), on the maximum tensile strength in laminated polyester matrix reinforced with fiberglass E short and random investigated, the pressure values are evaluated infiltration 30,45,60,75 and 90 psi for the RTM process of an air compressor adapted 2HP power, the laminates obtained by the above processes were 30 * 15 cm length and width and thickness was determined by the thickness of the mold in the case of RTM was approximately 3 mm. The obtained laminates specimens for tensile test were extracted according to ASTM standard D638-01. From the results it was determined that the increase in infiltration pressure in the range of study, increases the maximum tensile strength of the laminates obtained using the RTM process, in the range of 30 to 75 psi, and then present a slight decrease of the property to 90psi, this would depend on the permeability characteristics of the reinforcing layers and the phenomenon we call displacement, and therefore the lack of wetting of the fibers used by the resin. Higher values of tensile strength was reached at 75 psi (128.96 MPa), while the lowest was obtained at 30 psi (90.21MPa). In some cases detachment between fiber and matrix which supports the lack of moisture between components of the obtained compound is evident, it is demonstrated through micrographic evaluation. The results are confirmed by analysis of variance for a confidence level of 95%, the latter concludes that the pressure infiltration resin significantly influence the maximum tensile strength of the laminates of polyester resin and glass fiber obtained by RTM process.es_ES
dc.identifier.urihttps://hdl.handle.net/20.500.14414/2547
dc.language.isospaes_ES
dc.publisherUniversidad Nacional de Trujillo
dc.relation.ispartofseriesTMAT 9036;9036
dc.rightsinfo:eu-repo/semantics/openAccesses_ES
dc.rights.urihttp://creativecommons.org/licenses/by-nc-nd/2.5/pe/
dc.sourceUniversidad Nacional de Trujilloes_ES
dc.sourceRepositorio institucional - UNITRUes_ES
dc.subjectProceso de moldeoes_ES
dc.titleInfluencia de la presión de infiltración del proceso de moldeo por trasferencia de resina, sobre la resistencia a la tracción, de un compuesto de matriz poliéster reforzada con fibra de vidrioes_ES
dc.typeinfo:eu-repo/semantics/bachelorThesises_ES
thesis.degree.disciplineMateriales
thesis.degree.grantorUniversidad Nacional de Trujillo.Facultad de Ingeniería
thesis.degree.levelTítulo Profesional
thesis.degree.nameIngeniero de Materiales
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
RODRIGUEZ DANGELO, David Alessandro, SAUCEDO FERNANDEZ, Homero.pdf
Size:
4.25 MB
Format:
Adobe Portable Document Format
Description:
PROCESO DE MOLDEO POR TRANSFERENCIA DE RESINA
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
Tesis de Materiales