Tratamiento criogénico aplicado al aluminio 7075 pretratado con envejecido: efectos en la fuerzas de corte y rugosidad, utilizando diferentes parámetros de maquinado
| dc.contributor.advisor | Alcántara Alza, Víctor Manuel | |
| dc.contributor.author | Collantes Delgado, Walter Enmanuel | |
| dc.date.accessioned | 2025-04-28T14:48:19Z | |
| dc.date.available | 2025-04-28T14:48:19Z | |
| dc.date.issued | 2025-04 | |
| dc.description.abstract | Este trabajo de investigación tiene como finalidad explorar el efecto del envejecimiento más el tratamiento criogénico sobre la maquinabilidad de la aleación de aluminio A-7075 sometido a altas velocidades de corte. Se utilizaron muestras de aleación de aluminio 7075 adqiridas por el fabricante en condición de envejecido artificial T6 . Luego fueron tratadas criogénicamente (- 196◦C (DCT)) durante 48 h. Después del tratamiento térmico y criogénico, las muestras se cortaron con alta velocidad de corte utilizando un torno Lath-CNC. Los resultados muestran que la fuerza de corte de la aleación de aluminio 7075 muestran que existe una correlación positiva entre la fuerza de corte, la velocidad de corte y el avance; pero, Existe una correlación negativa entre la rugosidad de la superficie de la pieza de trabajo y la velocidad de corte. Cuando la velocidad de corte es de 1500 m/min, la rugosidad es de 0,73 μm, que es 0,01 μm menor que la de la superficie de aleación de aluminio 7075-T6. Los defectos superficiales de la pieza de trabajo después del corte son principalmente adhesión de virutas y marcas evidentes de avance. Al incrementarse cualquier parámetro de corte se incrementa la fuerza de corte en magnitudes diferente; es decir, todos los parámetros de corte guardan una relación directa con las tres componentes de la fuerza de corte, destacando la velocidad de corte. De acuerdo a la literatura especializada los resultados se explican en razón de que las muestras pretratadas con envejecido, cuando se tratan criogénicamente; El tamaño del precipitado de la aleación es aproximadamente igual o ligeramente menor que el tamaño de grano de la aleación. Sin tratamiento criogénico | |
| dc.description.abstract | This research work aims to explore the effect of aging plus cryogenic treatment on the machinability of aluminum alloy A-7075 subjected to high cutting speeds. Samples of aluminum alloy 7075 purchased by the manufacturer in artificial aging condition T6 were used. They were then cryogenically treated (- 196◦C (DCT)) for 48 h. After heat and cryogenic treatment, the samples were cut with high cutting speed using a Lath-CNC lathe. The results show that the cutting force of aluminum alloy 7075 shows that there is a positive correlation between cutting force, cutting speed and feed rate; but, There is a negative correlation between the surface roughness of the workpiece and cutting speed. When the cutting speed is 1500 m/min, the roughness is 0.73 μm, which is 0.01 μm lower than that of the surface of 7075-T6 aluminum alloy. The surface defects of the workpiece after cutting are mainly chip adhesion and obvious feed marks. Increasing any cutting parameter increases the cutting force in different magnitudes; that is, all cutting parameters have a direct relationship with the three components of the cutting force, with the cutting speed being the most important. According to the specialized literature, the results are explained by the fact that the samples pretreated with aging, when cryogenically treated; The size of the alloy precipitate is approximately equal to or slightly smaller than the grain size of the alloy. Without cryogenic treatment | |
| dc.format | application/pdf | |
| dc.identifier.uri | https://hdl.handle.net/20.500.14414/23906 | |
| dc.language.iso | spa | |
| dc.publisher | Universidad Nacional de Trujillo | |
| dc.publisher.country | PE | |
| dc.rights | info:eu-repo/semantics/openAccess | |
| dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | |
| dc.subject | TECHNOLOGY::Engineering mechanics | |
| dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.03.00 | |
| dc.title | Tratamiento criogénico aplicado al aluminio 7075 pretratado con envejecido: efectos en la fuerzas de corte y rugosidad, utilizando diferentes parámetros de maquinado | |
| dc.type | info:eu-repo/semantics/article | |
| dc.type.version | info:eu-repo/semantics/publishedVersion | |
| renati.advisor.dni | 17923116 | |
| renati.advisor.orcid | 0000-0001-8899-0296 | |
| renati.author.dni | 70479787 | |
| renati.discipline | 713046 | |
| renati.juror | Azabache Vasquez, Eduardo Fausto | |
| renati.juror | Palacios Guarniz, Segundo Jose | |
| renati.juror | Alcantara Alza, Victor Manuel | |
| renati.level | https://purl.org/pe-repo/renati/level#tituloProfesional | |
| renati.type | https://purl.org/pe-repo/renati/type#tesis | |
| thesis.degree.discipline | Ingenieria Mecanica | |
| thesis.degree.grantor | Universidad Nacional de Trujillo. Facultad de Ingenieria | |
| thesis.degree.name | Ingeniero Mecanico |