Influencia del porcentaje de reemplazo de relave aurífero sulfurado de un geopolímero sobre el porcentaje de arsénico lixiviado
| dc.contributor.advisor | Castillo Chung, Aldo Roger | |
| dc.contributor.author | Domínguez Sánchez, José Luis | |
| dc.contributor.author | Yengle Arce, Jean Franco Enrique | |
| dc.date.accessioned | 2024-04-17T14:40:56Z | |
| dc.date.available | 2024-04-17T14:40:56Z | |
| dc.date.issued | 2024-04 | |
| dc.description.abstract | La investigación se enfocó en determinar la influencia del reemplazo de relave aurífero sulfurado en la concentración de arsénico V liberado en solución de pastas geopoliméricas de concreto reciclado. A su vez se aplicaron métodos de caracterización mecánica y físico-química como: resistencia a la compresión ASTM C109, densidad superficial por dimensiones y análisis de grupos funcionales FTIR. Se destacó la aplicación de una metodología explicativa, aplicada y cuantitativa, con un diseño experimental de un solo factor. La muestra consistió en la formación de 40 pastas geopoliméricas de concreto reciclado con relación a/c de 0.55, de diferentes porcentajes de relave de reemplazo (5%, 10%, 15%, 20%) pasantes de malla Nº 200, activadas con solución de NaOH a 3M. La caracterización química se aplicó mediante los polvos obtenidos de las pastas conformadas, mediante el Método 1311: Procedimiento de lixiviación de características de toxicidad a edades de 7 y 28 días. Donde se realizó una lixiviación mediante un proceso de agitación continua durante aproximadamente 6 horas a temperatura ambiente. La sustancia líquida resultante se evaluó y cuantificó en términos de cationes. Entre la caracterización físico-química de los geopolímeros se obtuvieron una densidad aparente y una resistencia a la compresión optima de 2.02 g/cm3 y 23.12 MPa. Como resultados se obtuvo que, a mayores porcentajes de reemplazo de relave aurífero sulfuroso se generaron menores concentraciones de arsénico V lixiviado, manteniéndose los porcentajes de 15% y 20% con concentraciones de 0.010 mg/L y 0.008 mg/L respectivamente, en el margen de los límites establecidos por los Estándares de Calidad Ambiental (ECA). Alcanzando una concentración de arsénico V lixiviado ideal de 0.008 mg/L para el nivel 20% de reemplazo en pastas geopoliméricas de concreto reciclado con reemplazo de relave aurífero sulfuroso a 7 días. | |
| dc.description.abstract | The research is focused on determining the influence of the replacement of sulfide gold tailings on the concentration of arsenic V released in solution from geopolymer pastes of recycled concrete. At the same time, mechanical and physical-chemical characterization methods were applied, such as: ASTM C109 compressive strength, surface density by dimensions and FTIR functional group analysis. The application of an explanatory, applied and quantitative methodology was highlighted, with a single-factor experimental design. The sample consisted of the formation of 40 geopolymeric pastes of recycled concrete with a w/c ratio of 0.55, of different percentages of replacement tailings (5%, 10%, 15%, 20%) passing through mesh No. 200, activated with solution from NaOH to 3M. The chemical characterization was applied using the powders obtained from the formed pastes, using Method 1311: Leaching procedure for toxicity characteristics at ages of 7 and 28 days. Where leaching was carried out through a continuous stirring process for approximately 6 hours at room temperature. The resulting liquid substance was evaluated and quantified in terms of cations. Between the physical-chemical characterization of the geopolymers, an apparent density and an optimal compressive strength of 2.02 g/cm3 and 23.12 MPa were obtained. As results, it was obtained that, at higher replacement percentages of sulphurous gold tailings, lower concentrations of leached arsenic V were generated, maintaining the percentages of 15% and 20% with concentrations of 0.010 mg/L and 0.008 mg/L respectively, in the range. of the limits established by the Environmental Quality Standards (ECA). Reaching an ideal leached arsenic V concentration of 0.008 mg/L for the 20% replacement level in geopolymeric pastes of recycled concrete with replacement of sulphurous gold tailings at 7 days. | |
| dc.format | application/pdf | |
| dc.identifier.uri | https://hdl.handle.net/20.500.14414/21098 | |
| dc.language.iso | es | |
| dc.publisher | Universidad Nacional de Trujillo | |
| dc.publisher.country | PE | |
| dc.rights | info:eu-repo/semantics/openAccess | |
| dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | |
| dc.subject | TECHNOLOGY::Chemical engineering::Metallurgical process and manufacturing engineering::Metallurgical process engineering | |
| dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.00.00 | |
| dc.title | Influencia del porcentaje de reemplazo de relave aurífero sulfurado de un geopolímero sobre el porcentaje de arsénico lixiviado | |
| dc.type | info:eu-repo/semantics/bachelorThesis | |
| dc.type.version | info:eu-repo/semantics/publishedVersion | |
| renati.advisor.dni | 18132971 | |
| renati.advisor.orcid | 0000-0002-2270-1671 | |
| renati.author.dni | 42148779 | |
| renati.author.dni | 72104417 | |
| renati.discipline | 713026 | |
| renati.juror | Cortijo Garcia, Agusberto | |
| renati.juror | Castillo Chung, Aldo Roger | |
| renati.juror | Portilla Rodriguez, Hans | |
| renati.level | http://purl.org/pe-repo/renati/level#tituloProfesional | |
| renati.type | http://purl.org/pe-repo/renati/type#tesis | |
| thesis.degree.discipline | Ingenieria Metalugica | |
| thesis.degree.grantor | Universidad Nacional de Trujillo, Facultad de Ingenieria | |
| thesis.degree.name | Ingeniero Metalurgista |