Estudio de la temperatura de austemperizado en la obtención de la fundición ADI sobre la resistencia a la tracción, tensión de fluencia, ductilidad, resistencia al desgaste y dureza de una fundición nodular ASTM A536
| dc.contributor.advisor | Purizaga Fernández, Ismael Ignacio | |
| dc.contributor.author | Cerna Solano, Ariel | |
| dc.contributor.author | Vásquez Suárez, Gian Marco | |
| dc.date.accessioned | 2024-03-15T13:25:36Z | |
| dc.date.available | 2024-03-15T13:25:36Z | |
| dc.date.issued | 2024-03 | |
| dc.description.abstract | En la presente investigación se evaluó el efecto de la temperatura de austempering, en el rango de 240 a 400ºC por 45 minutos, en la fundición nodular o dúctil ASTM A536 austenizada a 900ºC por 40 minutos, sobre la dureza, resistencia a la tracción, tensión de fluencia, ductilidad y resistencia al desgaste. Se utilizaron probetas estandarizadas según norma ASTM E-10 para el ensayo de dureza, probetas según norma ASTM E-8 para el ensayo de tracción y probetas según norma ASTM G-77 para el ensayo de desgaste. Los valores experimentales obtenidos y el análisis estadístico de los mismos confirman el efecto significativo de la temperatura de austempering, a las condiciones de estudio, en la fundición nodular o dúctil ASTM A536 sobre las propiedades mecánicas evaluadas, de tal manera que, a una temperatura de 240ºC se obtienen los valores más altos de dureza, resistencia a la tracción, tensión de fluencia y resistencia al desgaste debido a que microestructuralmente está formada por nódulos de grafito y finas placas o agujas de ferrita dispersas en la austenita (H) metaestable que está enriquecida con carbono. Conforme aumenta la temperatura hasta 360ºC, las mismas propiedades mecánicas mencionadas disminuyen debido a que las agujas o placas de ferrita se van haciendo más gruesas distorsionando la matriz. Luego a 400ºC, se produce un ligero incremento en los valores de las propiedades mecánicas, debido a la precipitación del carbono expulsado de la ferrita en los flancos o bordes de los nódulos produciendo un encapsulamiento de esta zona. La ductilidad presenta un aumento conforme se incrementa la temperatura de austempering, debido a que las agujas o placas de ferrita que se van haciendo bastas son blandas. Los resultados obtenidos han sido contrastados con un análisis estadístico con un nivel de confianza de 95%. | |
| dc.description.abstract | In the present investigation, the effect of austempering temperature, in the range of 240 to 400ºC for 45 minutes, in nodular or ductile cast iron ASTM A536 austenitized at 900ºC for 40 minutes, on the hardness, tensile strength, tension of creep, ductility and wear resistance. Standardized specimens were used according to ASTM E-10 for the hardness test, specimens according to ASTM E-8 for the tensile test, and specimens according to ASTM G-77 for the wear test. The experimental values obtained and their statistical analysis confirm the significant effect of the austempering temperature, at the study conditions, in the nodular or ductile cast iron ASTM A536 on the mechanical properties evaluated, in such a way that, at a temperature of 240ºC, the highest values of hardness, tensile strength, yield stress and wear resistance are obtained because microstructurally it is formed by graphite nodules and fine ferrite plates or needles dispersed in the metastable austenite (H) that is enriched with carbon. As the temperature increases up to 360ºC, the same mechanical properties mentioned decrease because the ferrite needles or plates become thicker, distorting the matrix. Then at 400ºC, there is a slight increase in the values of the mechanical properties, due to the precipitation of the carbon expelled from the ferrite on the flanks or edges of the nodules, producing an encapsulation of this area. Ductility increases as the austempering temperature increases, because the ferrite needles or plates that become coarse are soft. The results obtained have been contrasted with a statistical analysis with a confidence level of 95%. | |
| dc.format | application/pdf | |
| dc.identifier.uri | https://hdl.handle.net/20.500.14414/20874 | |
| dc.language.iso | es | |
| dc.publisher | Universidad Nacional de Trujillo | |
| dc.publisher.country | PE | |
| dc.rights | info:eu-repo/semantics/openAccess | |
| dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | |
| dc.subject | TECHNOLOGY::Chemical engineering::Metallurgical process and manufacturing engineering::Metallurgical process engineering | |
| dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.00.00 | |
| dc.title | Estudio de la temperatura de austemperizado en la obtención de la fundición ADI sobre la resistencia a la tracción, tensión de fluencia, ductilidad, resistencia al desgaste y dureza de una fundición nodular ASTM A536 | |
| dc.type | info:eu-repo/semantics/bachelorThesis | |
| dc.type.version | info:eu-repo/semantics/publishedVersion | |
| renati.advisor.dni | 17806774 | |
| renati.advisor.orcid | 0000-0001-7434-7336 | |
| renati.author.dni | 70599132 | |
| renati.author.dni | 71259603 | |
| renati.discipline | 713026 | |
| renati.juror | Panta Mesones, Julio | |
| renati.juror | Castillo Chung, Aldo | |
| renati.juror | Purizaga Fernandez, Izmael | |
| renati.level | http://purl.org/pe-repo/renati/level#tituloProfesional | |
| renati.type | http://purl.org/pe-repo/renati/type#tesis | |
| thesis.degree.discipline | Ingenieria Metalurgica | |
| thesis.degree.grantor | Universidad Nacional de Trujillo, Facultad de Ingenieria | |
| thesis.degree.name | Ingeniero Metalurgista |