Influencia de la Adición de Fibras Vegetales Sobre la Resistencia a la Compresión y Flexión en Morteros Alcalinos Híbridos de Concreto Reciclado y Ladrillo de Arcilla
| dc.contributor.advisor | Vega Anticona, Alexander Yushepy | |
| dc.contributor.author | Graos Alva, Oscar Alejandro | |
| dc.contributor.author | Rodríguez Benites, Maria Paula | |
| dc.date.accessioned | 2024-04-23T19:40:37Z | |
| dc.date.available | 2024-04-23T19:40:37Z | |
| dc.date.issued | 2024-04 | |
| dc.description.abstract | El propósito de esta investigación fue determinar cómo influye la adición de fibras vegetales de Cabuya sobre la resistencia a la compresión y flexión en morteros alcalinos híbridos de concreto reciclado y ladrillo de arcilla. En donde se conformaron 120 morteros alcalinos híbridos; 60 cubos para ensayos de compresión ASTM C109 de dimensiones 50x50x50mm y 60 vigas para ensayos de flexión ASTM C348 de dimensiones 40x40x160mm. Se emplearon los parámetros de diseño de mezcla; morteros con relación a/c de 0.485, con proporción conglomerante híbrido y agregado fino de 1/3 (w/w). Se empleó concreto reciclado y ladrillo de arcilla pulverizados en proporción 30/70 (w/w), pasantes por malla No 400, y arena gruesa como agregado fino. También se empleó una solución de NaOH 8M para la activación alcalina. Se trabajó con fibras vegetales de especie agave sisalana, cabuya, de tipo discontinua de 2 cm, de orientación al azar y libres de daños superficiales. Estas se añadieron en niveles de 0%, 1%, 1.5% y 2 % en peso de conglomerante hibrido. Finalmente se caracterizaron de forma físico-química como mecánica mediante métodos SEMEDS, FTIR y ensayos de compresión y flexión a 7, 14 y 28 días con un número de 05 repeticiones de ensayo. Se obtuvo una resistencia a la compresión máxima de 17.18 MPa con nivel de 1.5%w de adición a 28 días de ensayo. Mientras que, para resistencia a la flexión máxima, se obtuvo 4.85 MPa con nivel de 2%w de adición a 28 días de ensayo. Concluyendo que a mayor %w de adición de fibras de cabuya se obtienen mayores esfuerzos mecánicos en morteros alcalinos híbridos en base a concreto reciclado y ladrillo de arcilla. | |
| dc.description.tableofcontents | The goal of this research was to determine how the addition of Cabuya plant fibers influences the compressive and flexural strength in hybrid alkaline mortars of recycled concrete and clay brick. 120 hybrid alkaline mortars were formed; 60 cubes for ASTM C109 compression tests with dimensions 50x50x50mm and 60 beams for ASTM C348 bending tests with dimensions 40x40x160mm. The mixture design parameters were used; mortars with a w/c ratio of 0.485, with a hybrid binder and fine aggregate ratio of 1/3 (w/w). Likewise, recycled concrete and pulverized clay brick were used in a 30/70 (w/w) proportion, both passing through No 400 mesh, and coarse sand as fine aggregate. As well as an 8M NaOH solution for alkaline activation. Vegetable fibers of the species agave sisalana, cabuya, discontinuous type of 2 cm, randomly oriented and free of surface damage, were used. Which were added at levels of 0%, 1%, 1.5% and 2% by weight of hybrid binder. Finally, they were characterized physically-chemically and mechanically through SEM-EDS and FTIR methods and compression and flexion tests at 7, 14 and 28 days with a number of 05 test repetitions. A maximum compressive strength of 17.18 MPa was obtained with a 1.5% w addition level after 28 days of testing. While, for maximum flexural strength, 4.85 MPa was obtained with a 2% w addition level at 28 days of testing. Concluding that the higher %w addition of cabuya fibers, the higher mechanical stresses are obtained in hybrid alkaline mortars based on recycled concrete and clay brick. | |
| dc.format | application/pdf | |
| dc.identifier.uri | https://hdl.handle.net/20.500.14414/21212 | |
| dc.language.iso | es | |
| dc.publisher | Universidad Nacional de Trujillo | |
| dc.publisher.country | PE | |
| dc.rights | info:eu-repo/semantics/openAccess | |
| dc.rights.uri | https://creativecommons.org/licenses/by-nc-nd/4.0/ | |
| dc.subject | TECHNOLOGY::Materials science | |
| dc.subject.ocde | https://purl.org/pe-repo/ocde/ford#2.00.00 | |
| dc.title | Influencia de la Adición de Fibras Vegetales Sobre la Resistencia a la Compresión y Flexión en Morteros Alcalinos Híbridos de Concreto Reciclado y Ladrillo de Arcilla | |
| dc.type | info:eu-repo/semantics/bachelorThesis | |
| dc.type.version | info:eu-repo/semantics/publishedVersion | |
| renati.advisor.dni | 18217780 | |
| renati.advisor.orcid | 0000-0002-0638-2391 | |
| renati.author.dni | 72038567 | |
| renati.author.dni | 76209678 | |
| renati.discipline | 713016 | |
| renati.juror | Chavez Novoa, Danny Mesias | |
| renati.juror | Otiniano Mendez, Santos Dionicio | |
| renati.juror | Vega Anticona, Alexander Yushepy | |
| renati.level | http://purl.org/pe-repo/renati/level#tituloProfesional | |
| renati.type | http://purl.org/pe-repo/renati/type#tesis | |
| thesis.degree.discipline | Ingenieria de Materiales | |
| thesis.degree.grantor | Universidad Nacional de Trujillo. Facultad de Ingenieria | |
| thesis.degree.name | Ingeniero de Materiales |