“Influencia del Porcentaje de Hidroxiapatita sobre la Resistencia al Impacto, Desgaste Adhesivo y Dureza en Biocompuestos a base de Polietileno de Alta Densidad”

Simple item page
dc.contributor.advisorChavez Novoa Danny Mesias
dc.contributor.authorCaballero Saucedo , Giorgiana Alexandra
dc.contributor.authorRodríguez Girón, Melanie Rosy
dc.date.accessioned2024-09-20T16:18:03Z
dc.date.available2024-09-20T16:18:03Z
dc.date.issued2024-09
dc.description.abstractLa presente investigación tuvo como objetivo determinar la influencia de la hidroxiapatita (HA) sobre la resistencia al impacto, el desgaste adhesivo y la dureza en biocompuestos a base de polietileno de alta densidad (HDPE). La hidroxiapatita se obtuvo a partir de cáscaras de huevo a las cuales se les realizó un proceso de molienda, fosfatado y calcinación. Se caracterizó el polvo resultante mediante Espectroscopía Infrarroja por Transformada de Fourier (FTIR), Análisis Termogravimétrico (TG) y Difracción de Rayos X (DRX) obteniendo los grupos funcionales característicos, la estabilidad química, los ángulos de difracción y los planos cristalográficos correspondientes, respectivamente, lo que demuestra que el polvo obtenido es hidroxiapatita. Los biocompuestos se formaron tomando como matriz al HDPE y como refuerzo a la HA al 10, 20, 30 y 40% en peso, mediante el proceso de extrusión a una temperatura aproximada de 220°C usando un equipo extrusor monohusillo de laboratorio. Los mejores resultados se obtuvieron para la adición del 20% en peso de HA en el biocompuesto, obteniendo una resistencia al impacto de 23.057 KJ/m2, que representa un 127% de aumento, además presentan un menor desgaste con una correspondiente pérdida de masa de 0.367g representando una disminución del 83% y una mayor dureza con un valor de 19.767 Shore D que indica un 17% de incremento con respecto a las muestras sin relleno de HA. Por lo que se concluye que la adición de hidroxiapatita en el biocompuesto influye mejorando las propiedades de resistencia al impacto, desgaste adhesivo y dureza, siendo el porcentaje óptimo de adición el 20% en peso.
dc.description.abstractThe research aimed to determine how hydroxyapatite (HA) influences impact resistance, wear adhesion and toughness in high-density polyethylene (HDPE)-biocomposites. Hydroxyapatite derived from eggshells underwent grinding, phosphating, and calcination processes. Characterization of the resulting powder involved Fourier Transform Infrared Spectroscopy (FTIR), Thermogravimetric Analysis (TG), and X-ray Diffraction (XRD) to identify characteristic functional groups, chemical stability, diffraction angles, and corresponding crystallographic planes, confirming the composition as hydroxyapatite. Biocomposites containing HDPE as matrix and HA as reinforcement at 10, 20, 30 and 40% by weight, through the extrusion process at a temperature of approximately 220°C using a laboratory single-screw extruder. the samples without HA filler. The best results achieved in the case of the addition of 20% by weight of HA in the biocomposite, with an impact resistance of 23.057 KJ/m2, which represents a 127% increase, as well as a reduced wear with a decrease in mass loss of 0.367g, representing a reduction of 83%, and a higher toughness with a value of 19.767 Shore D, showing a 17% increase with respect to Therefore, it was found that the addition of hydroxyapatite in the biocomposite improves the properties of impact resistance, wear adhesion and toughness, with an optimum addition percentage of 20% by weight.
dc.formatapplication/pdf
dc.identifier.urihttps://hdl.handle.net/20.500.14414/22377
dc.language.isospa
dc.publisherUniversidad Nacional de Trujillo
dc.publisher.countryPE
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rights.urihttps://creativecommons.org/licenses/by-nc-nd/4.0/
dc.subjectTECHNOLOGY::Materials science
dc.subject.ocdehttps://purl.org/pe-repo/ocde/ford#2.00.00
dc.title“Influencia del Porcentaje de Hidroxiapatita sobre la Resistencia al Impacto, Desgaste Adhesivo y Dureza en Biocompuestos a base de Polietileno de Alta Densidad”
dc.typeinfo:eu-repo/semantics/bachelorThesis
dc.type.versioninfo:eu-repo/semantics/publishedVersion
renati.advisor.dni80495980
renati.advisor.orcid0000-0002-8513-7764
renati.author.dni73986888
renati.author.dni75278127
renati.discipline713016
renati.jurorDiaz Diaz, Alex Fabian
renati.jurorOtiniano Mendez, Santos Dionicio
renati.jurorChavez Novoa, Danny Mesias
renati.levelhttp://purl.org/pe-repo/renati/level#tituloProfesional
renati.typehttp://purl.org/pe-repo/renati/type#tesis
thesis.degree.disciplineIngenieria de Materiales
thesis.degree.grantorUnioersidad Nacional de Trujillo. Facultad de Ingenieria
thesis.degree.nameIngeniero de Materiales
Files
Original bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
Caballero Saucedo y Rodriguez Giron.pdf
Size:
4.57 MB
Format:
Adobe Portable Document Format
Download
License bundle
Now showing 1 - 1 of 1
No Thumbnail Available
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
Tesis de Materiales